induction shrink fitting cam shaft gears
Shrink Fitting Cam Shaft Gears Objective To heat aluminum and steel camshaft gears to over 500F within 4 minutes for a shrink fitting application.Material 6” diameter, 2” thick steel and aluminum camshaft gears, “K” type thermocouple, digital thermomet…
-
induction shrink fit steel ring
Shrink fit steel ring Objective Heating a steel band to 1000 F (538 C) and inserting a carbon graphite ring in the center of the steel bandMaterial 4340 steel ring 8” (20.3cm) OD x 7.75” (19.7cm) ID, .895” (22.7mm) thick, carbon graphite ring insertTemp…
-
induction levitation melting steel balls
Levitation melting steel balls Objective Levitation of steel balls during the melting processMaterial 1010 low carbon steel balls ” (6.35mm) diameterTemperature 2800 F (1538 C)Frequency 195 kHzEquipment • Power of 30 kW induction heating system, equipped…
-
induction shrink fit bearings
Shrink Fit Bearings Objective To heat a roller bearing assembly for a shrink fitting applicationMaterial Steel bearings, diameters 1” to 3.5” (25.4 to 89mm)Temperature 300F (150C)Frequency 60 kHzEquipment Power of 25kW solid-state induction power supply …
-
induction shrink fit steel flange
Shrink Fit Steel Flange Objective To heat steel flange for heat shrink application. Reaching the desired temperature results in adequate expansion to allow for placing of the flange over a graphite seal.Material Graphite seal 1” (25.4mm) diameter steel fl…
-
induction shrink fit steel tube
Shrink Fit Steel Tube Objective Heating a steel tube to 500-1000F for a shrink-fitting application. Determine expansion (growth) of ID at varying temperatures.Material Steel tubes 7” OD x 4.75” ID x 5” heat zone Type ‘K’ thermocouple to measure temper…
-
induction hardening of bearing parts
INDUCTION HARDENING OF BEARING PARTS It is known that induction heating is effective in flow-line mass production that precludesresetting of equipment, or in individual production where the application of ordinaryheating methods is difficult.Induction hard…
-
heat treatment with induction heating of within pipes
HEAT TREATMENT WITH INDUCTION HEATING OF WITHIN PIPES Electrically welded pipes with an external diameter of 16-102 mm made from corrosionresistantsteels of the austenitic class after having been made on argon-arc welding mill(AAW) are at present heat-trea…
-
induction melting ticonium and nobilium
Melting Ticonium and Nobilium Objective: Crucible melting of Ticonium and Nobilium ingots within a period of 45 seconds. Four ingots of Nobilium are to be placed in a crucible (ID#6012) and heated, while a single ingot of Ticonium is placed in a crucible (…
-
induction melting aluminum for casting
Objective Heating a graphite crucible to 1292F (700C) to melt aluminum to liquid form for a casting applicationMaterial 9.8” (250mm) OD, 22.4” (570mm) long, 0.7” (17.5mm) thick Graphite crucible, approx. 92.5lb (42kg) of aluminumTemperature 1292 F (700C…