induction Heating is very popular for various of applications such as Annealing Bonding, Rubber/Metal Brazing , Cap Sealing ,Carbide Tipping, Catheter Tipping ,Crystal Pulling , Curing , Forging ,Getter Firing , Hardening , Heat Treating , Hot Forming ,Levitation ,Material Testing , Melting ,etal-glass Sealing , Metal-plastic Staking , MOCVD ,Pin Sealing,metal anneal, diathermanous shaping, high frequency quenching,metal high frequency jointing, medium smelting, high frequency soldering and brazing, heat smearing, heat plastic encapsulation,Induction Annealing, Bar end Induction heating, Induction Billet heating, Induction Bonding, Induction Brazing, Induction Curing of powder or aqueous coatings, Induction Forging, Induction Forming, Induction Getter Flashing, Graphite Suscepter Induction Heating, Induction Hardening, Induction Melting, Induction Normalizing, Induction Outgassing, Induction Preheating for Galvanizing, Induction Shrink Fitting, Induction Soldering, Induction Tempering, Pre-Owned Equipment etc
:There are 2 important parameters of Induction Heating Machine:one is the ouput power, anotheris the ouput vibrated frequency.
The higher the frequency, the thinner the heating penetration. So it is important to select the frequency of the machine according to the heating desire to achieve best heating effect.
The output power decide the heating speed, so power is selected according to the weight of the parts and the heating temperature and the heating speed desired.
:UIHM Induction Heating Machines have been used in huge area.They are very credible and Efficiency.
Applications:
Annealing
Heating and slow cooling of a material for reducing hardness and brittleness. Typically, the material has been hardened either through working or shaping rather than from an induction hardening process.
Billet Heating
Typically heating of solid bars of steel for pressing, hammering, or working into a shape to be machined into a final component.
Bonding
An attachment process that typically joins two metals together using a thermo set adhesive. A common use for bonding is the adhesion of body panels to reinforcement structures in automobiles.
Brazing
Joining of two or more items using a melted high temperature soldering material. The objects to be joined together and the braze material are both heated using high frequency induction.
Coating
Heating of a component prior to applying a covering material that requires heat for melting, fusing, and adhesion to the component. A typical use for coating is the application of epoxy the the surface of rebar used in buildings and roadways.
Curing
A drying process of a component that has had an applied paint or coating.
Expansion For Shrink Fit
Heating of a component to promote expansion. Typically the expanded object is placed on a second component. When the heated component cools it shrinks back to the original size providing a "shrink fit".
Forging
Heating of a material to change the shape. A typical application is tube heating to form a raw forging for machining to a final component.
Semi Solid Forming
Forming a component from a material that is not yet melted, but is soft enough to be formed into a new shape with a press and precision die.
Stress Relief
Heating and slow cooling of a component to relieve stress that has occurred in a previous process such as welding or forming.
Surface Harden
Heating for the purpose of achieving full hardness of metal in a shallow depth along the surface of the processed area. The hardened surface provides the basis for a wear surface while leaving the body of the component soft.
Tempering
Heating and slow cooling of a material for reducing hardness and brittleness. Typically, the material has been intentionally hardened either by an induction or furnace heating process.
Through Harden
Heating a component or zone on a component completely through the cross section of the material rather than hardening only a surface area.
| |
| |
| |
| |
| |
| |
| |
| |
| |
| |
Related Content
induction brazing SS steel by handheld induction coil
induction melting silicon and steel
magnesium oxide acidic furnace for induction melting glass
induction preheating gas pipeline by full air cooled clamp induction coil and DSP induction heater
induction melting with Titanium alloy pot by customized induction coil
induction melting aluminium for casting wire wheel
induction heating steel plate by pancake induction coil
induction heating steel knife
Hot
induction painting after induction bending for pipelines
induction heating steel plate
induction remove copper from aluminium
induction heating stator frame
induction heating graphite mould
difference between induction heating inner surface and outside surface of steel ring
induction heating steel pot bottom
induction heating for heat preservation
Newest Comment
No Comment
Post Comment